UV cured gel and method of making

ABSTRACT

A method of UV curing and corresponding resulting non-polymeric cross-linked gel are provided. The cross-linked gel can be combined with a medical device structure. The cross-linked gel can provide anti-adhesion characteristics, in addition to improved healing and anti-inflammatory response. The cross-linked gel is generally formed of a naturally occurring oil, or an oil composition formed in part of a naturally occurring oil, that is at least partially cured forming a cross-linked gel derived from at least one fatty acid compound. In addition, the oil composition can include a therapeutic agent component, such as a drug or other bioactive agent. The curing method can vary the application of UV light in both intensity and duration to achieve a desired amount of cross-linking forming the gel.

RELATED APPLICATIONS

This application claims priority to, and the benefit of, U.S.Provisional Application No. 60/613,808, filed Sep. 28, 2004, for allsubject matter common to both applications. The disclosure of saidprovisional application is hereby incorporated by reference in itsentirety. This application also relates to co-pending U.S. patentapplication Ser. No. 11/237,420, filed concurrently with thisapplication on Sep. 28, 2005.

FIELD OF THE INVENTION

The present invention relates to coatings for medical devices, or films,which are cured, and more particularly to a method of UV curing acoating or stand alone film formed at least in part of a non-polymericcross-linked gel cured a desired amount, and the resulting structureprovided by the curing process.

BACKGROUND OF THE INVENTION

Coatings and drugs, agents, or compounds are utilized in combinationwith a number of medical devices, and in particular with implantablemedical devices such as stents, stent-grafts, surgical meshes, vasculargrafts, and the like. Other devices such as vena cava filters andanastomosis devices may also be used with coatings having drugs, agents,or compounds therein. In addition, surgical medical film is often usedin surgical settings, such as in patients undergoing abdominal or pelviclaparotomy as an adjunct intended to reduce the incidence, extent, andseverity of postoperative adhesions between different tissues and organsand implantable medical devices such as soft tissue support membranesand mesh.

In general, such coatings and films are manufactured utilizing polymericbased materials. The coatings and films are formed using a number ofdifferent manufacturing techniques. However, there has been littleprogress in the manufacture of coatings or films utilizing non-polymericbased materials in a manner that can form the desired coating or film,with desired degradation properties, while maintaining some of theanti-inflammatory, non-inflammatory, and wound healing properties ofsome of the non-polymeric substances available.

More specifically, oils are occasionally briefly mentioned as being apotential carrier component for the delivery of a therapeutic from amedical device. However, there has been little development with regardto the determination of how to accomplish the provision of anon-polymeric coating containing a therapeutic, or even a non-polymericcoating maintaining its original anti-inflammatory, non-inflammatory, orwound healing properties. Some of these anti-inflammatory,non-inflammatory, and wound healing characteristics can be found in oilscontaining fatty acids, especially omega-3 fatty acids, such as fishoil. However, there is little known relating to methods for configuringnon-polymeric coatings to carry therapeutic agents in a manner thatresults in a predefined, desired, rate of degradation to provide for thecontrolled release of the therapeutic agent or the controlleddegradation of the coating.

SUMMARY OF THE INVENTION

What is desired is a method of making a non-polymeric biological oilbased coating on a medical device or in the form of a stand alone film,which exhibits properties such as anti-adhesion, anti-inflammation,non-inflammation, and enhanced wound healing, to the local tissue thatcan also be further enhanced with the application of one or moretherapeutic agents or medications for absorption into the tissue that isin contact with the coating or film. The method of making directlyinfluences the resulting coating or film and corresponding rate ofdegradation of the coating or film following implantation, and thus thecontrolled release of any therapeutic agents contained within. Themethod of curing also influences the level of inherentanti-inflammation, non-inflammation, and wound healing properties ofcertain biological oils that is able to be maintained after curing. Thepresent invention is directed toward further solutions to address thisneed.

Curing with respect to the present invention generally refers tothickening, hardening, or drying of a material brought about by heat,UV, or chemical means.

In accordance with one embodiment of the present invention, a method ofcuring to form a gel includes providing a non-polymeric substance to becured. An amount of cross-linking desired within the substance as aresult of curing is determined. UV light is applied at a selectedintensity for a selected time period based on the determination ofamount of cross-linking desired to achieve the desired amount ofcross-linking within the substance to form the gel.

In accordance with aspects of the present invention, the substance to becured can be an oil or oil composition. The substance to be cured cancontain fatty acids. The substance to be cured can include at least onetherapeutic agent. The agent can be any one or more of antioxidants,anti-inflammatory agents, anti-coagulant agents, drugs to alter lipidmetabolism, anti-proliferatives, anti-neoplastics, tissue growthstimulants, functional protein/factor delivery agents, anti-infectiveagents, imaging agents, anesthetic agents, chemotherapeutic agents,tissue absorption enhancers, anti-adhesion agents, germicides,analgesics, prodrugs, and antiseptics.

In accordance with further aspects of the present invention, the step ofdetermining includes selecting the amount of cross-linking based on adesired rate of degradation of the gel following implantation. Theapplication of UV light/heat occurs at a relatively greater intensity ifmore cross-linking is desired and at a relatively lesser intensity if alesser amount of cross-linking is desired. The application of UV lightoccurs for a relatively greater duration of time if more cross-linkingis desired and at a relatively lesser duration of time if a lesseramount of cross-linking is desired. A relatively faster rate ofdegradation provides for a relatively faster release of therapeuticagent contained within the gel, while a relatively slower rate ofdegradation provides for a relatively slower and more controlled releaseof therapeutic agent contained within the gel.

In accordance with further aspects of the present invention, thenon-polymeric substance to be cured at least partially includes at leastpartially cured oil to reduce the amount of time required to achieve thedesired amount of cross-linking.

In accordance with further aspects of the present invention, thecross-linked gel is configured to provide controlled release of atherapeutic agent component. The cross-linked gel is bio-absorbable. Thecross-linked gel maintains at least one property, such asanti-inflammatory properties, non-inflammatory properties, and woundhealing properties.

It should be noted that the term cross-linked gel, as utilized hereinwith reference to the present invention, refers to a gel that isnon-polymeric and is derived from an oil composition comprisingmolecules covalently cross-linked into a three-dimensional network byone or more of ester, ether, peroxide, and carbon-carbon bonds in asubstantially random configuration. In various preferred embodiments,the oil composition comprises a fatty acid molecule, a glyceride, andcombinations thereof.

In accordance with further aspects of the present invention, the methodcan include sterilizing the cross-linked gel with a method ofsterilization, such as ethylene oxide, gamma radiation, e-beam, steam,gas plasma, or vaporized hydrogen peroxide (VHP).

In accordance with one embodiment of the present invention, a UV curednon-polymeric gel includes a collection of non-polymeric cross-linksresulting from application of UV light/heat at a selected intensity fora selected duration to achieve a desired amount of cross-linking to formthe non-polymeric gel.

In accordance with aspects of the present invention, the gel can bederived from an oil or oil composition. The gel can be derived from asubstance comprising fatty acids. The gel can include at least onetherapeutic agent. The agent can be any one or more of antioxidants,anti-inflammatory agents, anti-coagulant agents, drugs to alter lipidmetabolism, anti-proliferatives, anti-neoplastics, tissue growthstimulants, functional protein/factor delivery agents, anti-infectiveagents, imaging agents, anesthetic agents, chemotherapeutic agents,tissue absorption enhancers, anti-adhesion agents, germicides,analgesics, prodrugs, and antiseptics.

In accordance with further aspects of the present invention, the gel isconfigured to maintain a desired rate of degradation of the gelfollowing implantation. The gel formed with application of UV light at arelatively higher intensity if more cross-linking is desired and at arelatively lower intensity if a lesser amount of cross-linking isdesired. The gel is formed with application of UV light/heat for arelatively greater duration of time if more cross-linking is desired andat a relatively lesser duration of time if a lesser amount ofcross-linking is desired.

In accordance with further aspects of the present invention, the gel isformed from at least partially pre-cured oil to reduce the amount oftime required to achieve the desired amount of cross-linking. Thecross-linked gel is configured to provide controlled release of atherapeutic agent component. The cross-linked gel is bio-absorbable. Thecross-linked gel maintains at least one property, such asanti-inflammatory properties, non-inflammatory properties, or woundhealing properties.

In accordance with further aspects of the present invention, the gel hasbeen sterilized with a method of sterilization including ethylene oxide,gamma radiation, e-beam, steam, gas plasma, or vaporized hydrogenperoxide (VHP).

In accordance with further aspects of the present invention, the gel isconfigured as a coating on a medical device or as a stand-alone film.Furthermore, the non-polymeric substance used to form the gel can bepre-treated to increase viscosity prior to curing.

BRIEF DESCRIPTION OF THE DRAWINGS

The aforementioned features and advantages, and other features andaspects of the present invention, will become better understood withregard to the following description and accompanying drawings, wherein:

FIG. 1 is a diagrammatic illustration of a cross-linked gel realized asa stand alone film, according to one embodiment of the presentinvention;

FIGS. 2A, 2B, and 2C are cross-sectional views of the cross-linked gelin accordance with one aspect of the present invention;

FIGS. 3A, 3B, 3C, 3D, 3E, and 3F are diagrammatic views of thecross-linked gel in accordance with another aspect of the presentinvention;

FIG. 4 is a flow chart illustrating a method of making the cross-linkedgel of the present invention, in accordance with one embodiment of thepresent invention;

FIGS. 5A and 5B are perspective and cross-sectional views of thecross-linked gel in combination with a medical device, in accordancewith one embodiment of the present invention;

FIG. 6 is a flow chart illustrating a method of combining thecross-linked gel with a medical device, in accordance with oneembodiment of the present invention;

FIG. 7 is a flow chart illustrating another variation of the method ofFIG. 6, in accordance with one embodiment of the present invention;

FIGS. 8A, 8B, and 8C are diagrammatic illustrations of the barriercoupled with various medical devices;

FIG. 9 is a flow chart illustrating one example method of curing to formthe cross-linked gel;

FIG. 10 is a graph showing a release rate of a cured coating accordingto an example embodiment disclosed herein;

FIG. 11 is a graph showing a drug release rate of cured coatingsaccording to an example embodiment disclosed herein;

FIG. 12 is a graph comparing the results illustrated in FIGS. 10 and 11;

FIG. 13 is a graph showing a drug release rate of a cured coatingaccording to an example embodiment disclosed herein;

FIG. 14 is a graph showing a drug release rate of a cured coatingaccording to an example embodiment disclosed herein; and

FIG. 15 is a graph showing a comparison of the results illustrated inFIGS. 13 and 14.

DETAILED DESCRIPTION

An illustrative embodiment of the present invention relates to theprovision of a coating or film that is a cured cross-linked gel and canexhibit anti-inflammatory properties, non-inflammatory properties,anti-adhesion properties, and/or wound healing properties, andcorresponding method of making. The cross-linked gel can be its ownmedical device (i.e., a stand alone film), or the cross-linked gel canbe combined with another medical device to provide the desiredcharacteristics, in addition to potentially delivering therapeuticagents. The cross-linked gel is generally formed of a naturallyoccurring oil, or an oil composition formed in part of a naturallyoccurring oil having fatty acids. In addition, the oil composition caninclude a therapeutic agent component, such as a drug or other bioactiveagent. The cross-linked gel is implantable in a patient, or applied onthe skin surface of the patient, for short term or long termapplications, and can include controlled release of the therapeuticagent. As implemented herein, the cross-linked gel is a non-polymericcross-linked gel derived at least in part from a fatty acid compound.

As utilized herein, the term “bio-absorbable” generally refers to havingthe property or characteristic of being able to penetrate the tissue ofa patient's body. In certain embodiments of the present inventionbio-absorption occurs through a lipophilic mechanism. The bio-absorbablesubstance is soluble in the phospholipid bi-layer of cells of bodytissue, and therefore impacts how the bio-absorbable substancepenetrates into the cells.

It should be noted that a bio-absorbable substance is different from abiodegradable substance. Biodegradable is generally defined as capableof being decomposed by biological agents, or capable of being brokendown by microorganisms or biological processes, in a manner that doesnot result in cellular uptake of the biodegradable substance.Biodegradation thus relates to the breaking down and distributing of asubstance through the patient's body, verses the penetration of thecells of the patient's body tissue. Biodegradable substances, such aspolymers, can cause inflammatory response due to either the parentsubstance or those substances formed during breakdown, and they may ormay not be absorbed by tissues. Bio-absorbable substances break downinto substances or components that do not cause an inflammatory responseand can be consumed by the cells forming the body tissues.

The phrase “controlled release” generally refers to the release of abiologically active agent in a predictable manner over the time periodof weeks or months, as desired and predetermined upon formation of thebiologically active agent on the medical device from which it is beingreleased. Controlled release includes the provision of an initial burstof release upon implantation, followed by the predictable release overthe aforementioned time period.

With regard to the aforementioned oils, it is generally known that thegreater the degree of unsaturation in the fatty acids the lower themelting point of a fat, and the longer the hydrocarbon chain the higherthe melting point of the fat. A polyunsaturated fat, thus, has a lowermelting point, and a saturated fat has a higher melting point. Thosefats having a lower melting point are more often oils at roomtemperature. Those fats having a higher melting point are more oftenwaxes or solids at room temperature. Therefore, a fat having thephysical state of a liquid at room temperature is an oil. In general,polyunsaturated fats are liquid oils at room temperature, and saturatedfats are waxes or solids at room temperature.

Polyunsaturated fats are one of four basic types of fat derived by thebody from food. The other fats include saturated fat, as well asmonounsaturated fat and cholesterol. Polyunsaturated fats can be furthercomposed of omega-3 fatty acids and omega-6 fatty acids. Under theconvention of naming the unsaturated fatty acid according to theposition of its first double bond of carbons, those fatty acids havingtheir first double bond at the third carbon atom from the methyl end ofthe molecule are referred to as omega-3 fatty acids. Likewise, a firstdouble bond at the sixth carbon atom is called an omega-6 fatty acid.There can be both monounsaturated and polyunsaturated omega fatty acids.

Omega-3 and omega-6 fatty acids are also known as essential fatty acidsbecause they are important for maintaining good health, despite the factthat the human body cannot make them on its own. As such, omega-3 andomega-6 fatty acids must be obtained from external sources, such asfood. Omega-3 fatty acids can be further characterized as containingeicosapentaenoic acid (EPA), docosahexanoic acid (DHA), andalpha-linolenic acid (ALA). Both EPA and DHA are known to haveanti-inflammatory effects and wound healing effects within the humanbody.

Oil that is hydrogenated becomes a waxy solid. Attempts have been madeto convert the polyunsaturated oils into a wax or solid to allow the oilto adhere to a device for a longer period of time. One such approach isknown as hydrogenation, which is a chemical reaction that adds hydrogenatoms to an unsaturated fat (oil) thus saturating it and making it solidat room temperature. This reaction requires a catalyst, such as a heavymetal, and high pressure. The resultant material forms anon-cross-linked semi-solid. Hydrogenation can reduce or eliminateomega-3 fatty acids, and any therapeutic effects (both anti-inflammatoryand wound healing) they offer.

For long term controlled release applications, polymers, as previouslymentioned, have been utilized in combination with a therapeutic agent.Such a combination provides a platform for the controlled long termrelease of the therapeutic agent from a medical device. However,polymers have been determined to themselves cause inflammation in bodytissue. Therefore, the polymers often must include at least onetherapeutic agent that has an anti-inflammatory effect to counter theinflammation caused by the polymer delivery agent. In addition, patientsthat received a polymer-based implant must also follow a course of longterm systemic anti-platelet therapy, on a permanent basis, to offset thethrombogenic properties of the non-absorbable polymer. A significantpercentage of patients that receive such implants are required toundergo additional medical procedures, such as surgeries (whetherrelated follow-up surgery or non-related surgery) and are required tostop their anti-platelet therapy. This can lead to a thrombotic event,such as stroke, which can lead to death. Use of the inventive coatingdescribed herein can negate the necessity of anti-platelet therapy, andthe corresponding related risks described, because there is nothrombogenic polymer reaction to the coating. Other polymer implantpatients must follow a course of systemic anti-inflammatory therapy, tooffset the inflammatory properties of the non-absorbable polymer.Typical anti-inflammatory agents are immunosupressants and systemicdelivery of anti-inflammatory agents can sometimes lead to additionalmedical complications, such as infection or sepsis, which can lead tolong term hospitalization or death. Use of the non-polymericcross-linked gel of the inventive coating described herein may alsonegate the necessity of anti-inflammatory therapy, and the correspondingrelated risks described, because there is no inflammatory reaction to anoil barrier formed in accordance with the present invention.

In addition, some curing methods have been indicated to have detrimentaleffects on the therapeutic agent combined with the omega-3 fatty acid,making them partially or completely ineffective. As such, oils, and morespecifically oils containing omega-3 fatty acids, have been utilized asa delivery agent for the short term uncontrolled release of atherapeutic agent, so that minimal or no curing is required. However,there are no known uses of oils containing omega-3 fatty acids forcombination with a therapeutic agent in a controlled release applicationthat makes use of the therapeutic benefits of the omega-3 fatty acids.Further, some application of UV light to the omega-3 fatty acids to curethe oil can lessen the total therapeutic effectiveness of the omega-3fatty acids, but not eliminate the therapeutic effectiveness. Onecharacteristic that can remain after certain curing by UV methods is thenon-inflammatory response of the tissue when exposed to the curedomega-3 fatty acid material. As such, an oil containing omega-3 fattyacids can be exposed to UV light for curing purposes, and still maintainsome or even a majority of the therapeutic effectiveness of the omega-3fatty acids. In addition, although the therapeutic agent combined withthe omega-3 fatty acid and cured with the omega-3 fatty acid can berendered partially ineffective, the portion remaining of the therapeuticagent can, in accordance with the present invention, maintainpharmacological activity and in some cases be more effective than anequivalent quantity of agent delivered with other barrier or coatingmaterials.

It should be noted that as utilized herein to describe the presentinvention, the terms vitamin E, vitamin E compound, andalpha-tocopherol, are intended to refer to the same or substantiallysimilar substance, such that they are interchangeable and the use of oneincludes an implicit reference to both. Further included in associationwith the term vitamin E are such variations including but not limited toone or more of alpha-tocopherol, beta-tocopherol, delta-tocopherol,gamma-tocopherol, alpha-tocotrienol, beta-tocotrienol,delta-tocotrienol, gamma-tocotrienol, alpha-tocopherol acetate,beta-tocopherol acetate, gamma-tocopherol acetate, delta-tocopherolacetate, alpha-tocotrienol acetate, beta-tocotrienol acetate,delta-tocotrienol acetate, gamma-tocotrienol acetate, alpha-tocopherolsuccinate, beta-tocopherol succinate, gamma-tocopherol succinate,delta-tocopherol succinate, alpha-tocotrienol succinate,beta-tocotrienol succinate, delta-tocotrienol succinate,gamma-tocotrienol succinate, mixed tocopherols, vitamin E TPGS,derivatives, analogs and pharmaceutically acceptable salts thereof.

FIGS. 1 through 9, wherein like parts are designated by like referencenumerals throughout, illustrate an example embodiment of a non-polymericbiological oil cross-linked gel cured to form a coating or film usingultraviolet (UV) light according to the present invention. Although thepresent invention will be described with reference to the exampleembodiments illustrated in the figures, it should be understood thatmany alternative forms can embody the present invention. One of ordinaryskill in the art will additionally appreciate different ways to alterthe parameters of the embodiments disclosed, such as the size, shape, ortype of elements or materials, in a manner still in keeping with thespirit and scope of the present invention.

FIG. 1 illustrates a non-polymeric cross-linked gel 10 in accordancewith one embodiment of the present invention. The cross-linked gel 10 isflexible, to the extent that it can be placed in a flat, curved, orrolled, configuration within a patient. The cross-linked gel 10 isimplantable, for both short term and long term applications. Dependingon the particular formulation of the cross-linked gel 10, thecross-linked gel 10 will be present after implantation for a period ofhours to days, or possibly months.

The cross-linked gel 10 is formed of an oil component. The oil componentcan be either an oil, or an oil composition. The oil component can be anaturally occurring oil, such as fish oil, cod liver oil, cranberry oil,or other oils having desired characteristics. One example embodiment ofthe present invention makes use of a fish oil in part because of thehigh content of omega-3 fatty acids, which provide healing support fordamaged tissue, as discussed below. The fish oil also serves as ananti-adhesion agent. In addition, the fish oil maintainsanti-inflammatory or non-inflammatory properties as well. The presentinvention is not limited to formation of the film or gel with fish oilas the naturally occurring oil. However, the following description makesreference to the use of fish oil as one example embodiment. Othernaturally occurring oils can be utilized in accordance with the presentinvention as described herein.

It should be noted that as utilized herein, the term fish oil fatty acidincludes but is not limited to omega-3 fatty acid, fish oil fatty acid,free fatty acid, esters of fish oil, triglycerides, or a combinationthereof. The fish oil fatty acid includes one or more of arachidic acid,gadoleic acid, arachidonic acid, eicosapentaenoic acid, docosahexaenoicacid or derivatives, analogs and pharmaceutically acceptable saltsthereof. Furthermore, as utilized herein, the term free fatty acidincludes but is not limited to one or more of butyric acid, caproicacid, caprylic acid, capric acid, lauric acid, myristic acid, palmiticacid, palmitoleic acid, stearic acid, oleic acid, vaccenic acid,linoleic acid, alpha-linolenic acid, gamma-linolenic acid, behenic acid,erucic acid, lignoceric acid, analogs and pharmaceutically acceptablesalts thereof. The naturally occurring oils, including fish oil, arecured as described herein to form a hydrophobic cross-linked gel,creating the cross-linked gel 10.

It should further be noted that FIG. 1 represents merely one embodimentof the cross-linked gel 10. The cross-linked gel 10 serves as abiological oil barrier and, depending on degree of cure, can also serveas a physical barrier, as depicted. The biological oil barrier isrepresented by the application of the fatty acid based oil, such as fishoil, onto a medical device. Such a configuration provides a biologicaloil cross-linked gel that provides a non-inflammatory oranti-inflammatory barrier coating. Using a number of different methodsas described below, the biological oil can be cured to create anon-polymeric cross-linked gel. In the instance of the medical devicetaking the form of a surgical mesh, the biological oil can be cured tothe extent that the cells or pores of the mesh are substantially orcompletely bridged by the cured biological oil creating a physicalbarrier. With such a configuration there remains some biological oilthat is not cured but is interdispersed within the cured oil andmaintains the biological oil cross-linked gel as well. Thus, substantialcuring creates both a biological oil cross-linked gel and a physicalbarrier. The physical barrier provides anti-adhesive properties of thebarrier as discussed herein. Additional embodiments can include theprovision of the substantially cured oil forming the biological oilcross-linked gel with physical layer, and then a subsequent applicationof the biological oil as a top coat. This creates a more substantialbiological oil cross-linked gel supported by the combination biologicaloil cross-linked gel and physical cross-linked gel.

One aspect of the cross-linked gel 10 mentioned above is that it hasanti-adhesion characteristics or properties. By anti-adhesion, what ismeant is a characteristic whereby the incidence, extent, and severity ofpostoperative adhesions, or lacerations or other tissue injuries,between different tissues and organs is reduced. The anti-adhesioncharacteristic results from the materials used to form the cross-linkedgel 10.

More specifically, the cross-linked gel 10 provides a lubricious oranti-adhesive surface against tissue. The cross-linked gel 10 itself, inits substantially cured configuration, can provide a physicalanti-adhesion barrier between two sections of tissue, or thecross-linked gel 10 can form an anti-adhesion surface on a medicaldevice, such as the mesh 40. The use of the naturally occurring oil,such as fish oil, provides extra lubrication to the surface of themedical device, which helps to reduce injury. With less injury, there isless of an inflammatory response, and less healing required. Thebiological oil barrier created by the fatty acid oil derivedcross-linked gel likewise provides anti-inflammatory properties andnon-inflammatory properties, thus reducing the occurrence ofinflammatory response and also adhesions due to inflammation. The oilysurface of the cross-linked gel 10 provides the anti-adhesioncharacteristics. One of ordinary skill in the art will appreciate thatdifferent oils will have different anti-adhesive properties, and theoils can be modified to be more liquefied or more solid or waxy, asdesired. Accordingly, the degree of anti-adhesive properties offered bythe cross-linked gel 10 can vary. The modification of the oils from amore liquid physical state to a more solid, but still flexible, physicalstate is implemented through the curing process. As the oils are cured,especially in the case of fatty acid-based oils such as fish oil,cross-links form creating a gel. As the curing process is performed overincreasing time durations and/or increasing temperature or UV lightexposure conditions, more cross-links form transitioning the gel from arelatively liquid gel to a relatively solid-like, but still flexible,gel structure.

Another aspect of the present invention is that the cross-linked gel 10is formed of the bio-absorbable material, such as naturally occurringfish oil, in accordance with the example embodiment described herein.The bio-absorbable properties of the naturally occurring oil enable thecross-linked gel 10 to be absorbed by the cells of the body tissue(i.e., bio-absorbable). In example embodiments of the present invention,the bio-absorbable cross-linked gel contains lipids, many of whichoriginate as triglycerides. It has previously been demonstrated thattriglyceride byproducts, such as partially hydrolyzed triglycerides andfatty acid molecules can integrate into cellular membranes and enhancethe solubility of drugs into the cell. Whole triglycerides are known notto enhance cellular uptake as well as partially hydrolyzed triglyceride,because it is difficult for whole triglycerides to cross cell membranesdue to their relatively larger molecular size. Vitamin E compounds canalso integrate into cellular membranes resulting in decreased membranefluidity and cellular uptake.

Compounds that move too rapidly through a tissue may not be effective inproviding a sufficiently concentrated dose in a region of interest.Conversely, compounds that do not migrate in a tissue may never reachthe region of interest. Cellular uptake enhancers such as fatty acidsand cellular uptake inhibitors such as alpha-tocopherol can be usedalone or in combination to provide an effective transport of a givencompound to a given region or location. Both fatty acids andalpha-tocopherol are accommodated by the cross-linked gel of the presentinvention described herein. Accordingly, fatty acids andalpha-tocopherol can be combined in differing amounts and ratios tocontribute to a cross-linked gel in a manner that provides control overthe cellular uptake characteristics of the cross-linked gel and anytherapeutic agents mixed therein.

For example, the amount of alpha-tocopherol can be varied in thecross-linked gel. Alpha-tocopherol (vitamin E compound) is known to slowautoxidation in fish oil by reducing hydroperoxide formation, whichresults in a decrease in the amount of cross-linking in cured fish oil.It has been shown that even with fewer cross-links, the addition ofvarying amounts of alpha-tocopherol can be used to increase the time inwhich the cross-linked gel degrades compared to a cross-linked gel offish oil alone. The addition of alpha-tocopherol to the oil or oilcomposition prior to forming the cross-linked gel can result in fewercross-links when compared with the oil without alpha-tocopherol.Although there are fewer cross-links, the degradation period is extendedwith the alpha-tocopherol added. In addition alpha-tocopherol can beused to increase solubility of drugs in the fish oil forming thecross-linked gel. Thus, varying the amount of alpha-tocopherol presentin the cross-linked gel can impact the resulting formation.Alpha-tocopherol can actually protect the therapeutic drug duringcuring, which increases the resulting drug load in the cross-linked gelafter curing. Furthermore, with certain therapeutic drugs, the increaseof alpha-tocopherol in the cross-linked gel serves to slow and extenddrug release due to the increased solubility of the drug in thealpha-tocopherol component of the cross-linked gel. This reflects thecellular uptake inhibitor functionality of alpha-tocopherol, in that theuptake of the drug is slowed and extended over time.

It should further be emphasized that the bio-absorbable nature of thecross-linked gel results in the cross-linked gel 10 being completelyabsorbed over time by the cells of the body tissue. There are nosubstances in the cross-linked gel, or break down products of thecross-linked gel, that induce an inflammatory response. The cross-linkedgel 10 is generally composed of, or derived from, omega-3 fatty acidsbound to triglycerides, potentially also including a mixture of freefatty acids and vitamin E compounds (alpha-tocopherol). Thetriglycerides are broken down by lipases (enzymes) which result in freefatty acids that can than be transported across cell membranes.Subsequently, fatty acid metabolism by the cell occurs to metabolize anysubstances originating with the cross-linked gel. The bio-absorbablenature of the cross-linked gel of the present invention results in thecross-linked gel being absorbed over time, leaving only an underlyingdelivery or other medical device structure that is biocompatible. Thereis no foreign body inflammatory response to the bio-absorbablecross-linked gel.

Although the present invention is bio-absorbable to the extent that thecross-linked gel 10 experiences the uptake into or through body tissues,in the specific embodiment described herein formed using naturallyoccurring oils, the exemplar oils are also lipid based oils. The lipidcontent of the oils provides a highly bio-absorbable cross-linked gel10. More specifically, there is a phospholipids layer in each cell ofthe body tissue. The fish oil, and equivalent oils, contain lipids aswell. There is a lipophilic action that results where the lipids areattracted by each other in an effort to escape the aqueous environmentsurrounding the lipids.

A further aspect of the cross-linked gel 10 is that the specific type ofoil can be varied, and can contain elements beneficial to healing. Thecross-linked gel also provides a natural scaffold for cellular growthand remodeling with clinical applications in general surgery, spinalrepair, orthopedic surgeries, tendon and ligament repairs, gynecologicaland pelvic surgeries, and nerve repair applications. The addition oftherapeutic agents to the cross-linked gels used in these applicationscan be utilized for additional beneficial effects, such as pain reliefor infection minimization. In addition, non-surgical applicationsinclude external wound care, such as a treatment for burns or skinulcers, without therapeutics as a clean, non-permeable, non-adhesive,anti-inflammatory, non-inflammatory dressing, or with added therapeuticsfor additional beneficial effects. The cross-linked gel may also be usedas a transdermal drug delivery patch.

The process of wound healing involves tissue repair in response toinjury and it encompasses many different biologic processes, includingepithelial growth and differentiation, fibrous tissue production andfunction, angiogenesis, and inflammation. The inventive cross-linked gelhas been shown in an animal model not to produce an inflammatoryresponse, but still provide excellent cellular overgrowth with little tono fibrous capsule formation. Accordingly, the cross-linked gel providesan excellent material suitable for wound healing applications.

Another aspect of the cross-linked gel 10 mentioned above is that thecross-linked gel 10 can contain therapeutic agents for delivery to thebody tissue. Therapeutic agents have been delivered to a targetedlocation in a human utilizing a number of different methods in the past.For example, agents may be delivered nasally, transdermally,intravenously, orally, or via other conventional methods. Delivery mayvary by release rate (i.e., quick release or slow release). Delivery mayalso vary as to how the drug is administered. Specifically, a drug maybe administered locally to a targeted area, or administeredsystemically.

As utilized herein, the phrase “therapeutic agent(s)” refers to a numberof different drugs or agents available, as well as future agents thatmay be beneficial for use with the cross-linked gel of the presentinvention. Therapeutic agents can be added to the cross-linked gel 10,and/or the medical device in combination with the cross-linked gel 10 asdiscussed herein. The therapeutic agent component can take a number ofdifferent forms including anti-oxidants, anti-inflammatory agents,anti-coagulant agents, drugs to alter lipid metabolism,anti-proliferatives, anti-neoplastics, tissue growth stimulants,functional protein/factor delivery agents, anti-infective agents,anti-imaging agents, anesthetic agents, therapeutic agents, tissueabsorption enhancers, anti-adhesion agents, germicides, antiseptics,analgesics, prodrugs, and any additional desired therapeutic agents suchas those listed in Table 1 below.

TABLE 1 CLASS EXAMPLES Antioxidants Alpha-tocopherol, lazaroid,probucol, phenolic antioxidant, resveretrol, AGI-1067, vitamin EAntihypertensive Agents Diltiazem, nifedipine, verapamilAntiinflammatory Agents Glucocorticoids (e.g. dexamethazone,methylprednisolone), leflunomide, NSAIDS, ibuprofen, acetaminophen,hydrocortizone acetate, hydrocortizone sodium phosphate,macrophage-targeted bisphosphonates Growth Factor Angiopeptin, trapidil,suramin Antagonists Antiplatelet Agents Aspirin, dipyridamole,ticlopidine, clopidogrel, GP IIb/IIIa inhibitors, abcximab AnticoagulantAgents Bivalirudin, heparin (low molecular weight and unfractionated),wafarin, hirudin, enoxaparin, citrate Thrombolytic Agents Alteplase,reteplase, streptase, urokinase, TPA, citrate Drugs to Alter LipidFluvastatin, colestipol, lovastatin, Metabolism (e.g. statins)atorvastatin, amlopidine ACE Inhibitors Elanapril, fosinopril,cilazapril Antihypertensive Agents Prazosin, doxazosinAntiproliferatives and Cyclosporine, cochicine, mitomycin C,Antineoplastics sirolimus micophenonolic acid, rapamycin, everolimus,tacrolimus, paclitaxel, QP-2, actinomycin, estradiols, dexamethasone,methatrexate, cilostazol, prednisone, cyclosporine, doxorubicin,ranpirnas, troglitzon, valsarten, pemirolast, C-MYC antisense,angiopeptin, vincristine, PCNA ribozyme, 2-chloro-deoxyadenosine Tissuegrowth stimulants Bone morphogeneic protein, fibroblast growth factorPromotion of hollow Alcohol, surgical sealant polymers, organ occlusionor polyvinyl particles, 2-octyl cyano- thrombosis acrylate, hydrogels,collagen, liposomes Functional Protein/Factor Insulin, human growthhormone, estradiols, delivery nitric oxide, endothelial progenitor cellantibodies Second messenger Protein kinase inhibitors targetingAngiogenic Angiopoetin, VEGF Anti-Angiogenic Endostatin Inhibitation ofProtein Halofuginone, prolyl hydroxylase Synthesis/ECM formationinhibitors, C-proteinase inhibitors Antiinfective Agents Penicillin,gentamycin, adriamycin, cefazolin, amikacin, ceftazidime, tobramycin,levofloxacin, silver, copper, hydroxyapatite, vancomycin, ciprofloxacin,rifampin, mupirocin RIP, kanamycin, brominated furonone, algaebyproducts, bacitracin, oxacillin, nafcillin, floxacillin, clindamycin,cephradin, neomycin, methicillin, oxytetracycline hydro- chloride,Selenium. Gene Delivery Genes for nitric oxide synthase, human growthhormone, antisense oligonucleotides Local Tissue perfusion Alcohol, H2O,saline, fish oils, vegetable oils, liposomes Nitric oxide Donor NCX4016 - nitric oxide dono Derivatives derivative of aspirin, SNAP GasesNitric oxide, compound solutions Imaging Agents Halogenated xanthenes,diatrizoate meglumine, diatrizoate sodium Anesthetic Agents Lidocaine,benzocaine Descaling Agents Nitric acid, acetic acid, hypochloriteAnti-Fibrotic Agents Interferon gamma - 1b, Interluekin - 10Immunosuppressive/ Cyclosporine, rapamycin, mycophenolateImmunomodulatory Agents motefil, leflunomide, tacrolimus, tranilast,interferon gamma-1b, mizoribine Chemotherapeutic Agents Doxorubicin,paclitaxel, tacrolimus, sirolimus, fludarabine, ranpirnase TissueAbsorption Fish oil, squid oil, omega 3 fatty acids, Enhancers vegetableoils, lipophilic and hydrophilic solutions suitable for enhancingmedication tissue absorption, distribution and permeation Anti-AdhesionAgents Hyaluronic acid, human plasma derived surgical sealants, andagents comprised of hyaluronate and carboxymethylcellulose tha arecombined with dimethylamino- propyl, ehtylcarbodimide, hydro- chloride,PLA, PLGA Ribonucleases Ranpirnase Germicides Betadine, iodine, slivernitrate, furan derivatives, nitrofurazone, benzalkonium chloride,benzoic acid, salicylic acid, hypochlorites, peroxides, thiosulfates,salicylanilide Antiseptics Selenium Analgesics Bupivicaine, naproxen,ibuprofen, acetylsalicylic acid

Some specific examples of therapeutic agents useful in theanti-restenosis realm include cerivastatin, cilostazol, fluvastatin,lovastatin, paclitaxel, pravastatin, rapamycin, a rapamycin carbohydratederivative (for example, as described in US Patent ApplicationPublication 2004/0235762), a rapamycin derivative (for example, asdescribed in U.S. Pat. No. 6,200,985), everolimus, seco-rapamycin,seco-everolimus, and simvastatin. With systemic administration, thetherapeutic agent is administered orally or intravenously to besystemically processed by the patient. However, there are drawbacks to asystemic delivery of a therapeutic agent, one of which is that thetherapeutic agent travels to all portions of the patient's body and canhave undesired effects at areas not targeted for treatment by thetherapeutic agent. Furthermore, large doses of the therapeutic agentonly amplify the undesired effects at non-target areas. As a result, theamount of therapeutic agent that results in application to a specifictargeted location in a patient may have to be reduced when administeredsystemically to reduce complications from toxicity resulting from ahigher dosage of the therapeutic agent.

Accordingly, an alternative to the systemic administration of atherapeutic agent is the use of a targeted local therapeutic agentdelivery approach. With local delivery of a therapeutic agent, thetherapeutic agent is administered using a medical device or apparatus,directly by hand, or sprayed on the tissue, at a selected targetedtissue location of the patient that requires treatment. The therapeuticagent emits, or is otherwise delivered, from the medical deviceapparatus, and/or carrier, and is applied to the targeted tissuelocation. The local delivery of a therapeutic agent enables a moreconcentrated and higher quantity of therapeutic agent to be delivereddirectly at the targeted tissue location, without having broadersystemic side effects. With local delivery, the therapeutic agent thatescapes the targeted tissue location dilutes as it travels to theremainder of the patient's body, substantially reducing or eliminatingsystemic side effects.

Targeted local therapeutic agent delivery using a medical device can befurther broken into two categories, namely, short term and long termranging generally within a matter of seconds or minutes to a few days orweeks to a number of months. Typically, to achieve the long termdelivery of a therapeutic agent, the therapeutic agent must be combinedwith a delivery agent, or otherwise formed with a physical impediment asa part of the medical device, to slow the release of the therapeuticagent.

Prior attempts to create films and drug delivery platforms, such as inthe field of stents, primarily make use of high molecular weightsynthetic polymer based materials to provide the ability to bettercontrol the release of the therapeutic agent. Essentially, the polymerin the platform releases the drug or agent at a predetermined rate onceimplanted at a location within the patient. Regardless of how much ofthe therapeutic agent would be most beneficial to the damaged tissue,the polymer releases the therapeutic agent based on properties of thepolymer. Accordingly, the effect of the therapeutic agent issubstantially local at the surface of the tissue making contact with themedical device having the coating. In some instances the effect of thetherapeutic agent is further localized to the specific locations of, forexample, stent struts pressed against the tissue location being treated.These prior approaches can create the potential for a localized toxiceffect.

The cross-linked gel 10 of the present invention, however, makes use ofthe natural oils to form a non-polymeric natural oil based therapeuticagent delivery platform, if desired. Furthermore, the cross-linked gel10 can be formed in a manner that creates the potential for controlledlong term release of a therapeutic agent, while still maintaining thebenefits of the natural oil component of the cross-linked gel 10.

More specifically, it is known that oil that is oxygenated becomes awaxy solid. Attempts have been made to convert the polyunsaturated oilsinto a wax or solid to allow the oil to adhere to a device for a longerperiod of time. One such approach applies the oil to the medical deviceand allows the oil to dry.

With the present invention, and in the field of soft tissueapplications, and in part because of the lipophilic mechanism enabled bythe bio-absorbable lipid based cross-linked gel 10 of the presentinvention, the uptake of the therapeutic agent is facilitated by thedelivery of the therapeutic agent to the cell membrane by thebio-absorbable cross-linked gel 10. Further, the therapeutic agent isnot freely released into the body fluids, but rather, is delivereddirectly to the cells and tissue. In prior configurations using polymerbased coatings, the drugs were released at a rate regardless of thereaction or need for the drug on the part of the cells receiving thedrug.

In addition, when the oil provided to form the cross-linked gel 10 is anaturally occurring oil containing the omega-3 fatty acids (includingDHA and EPA), the process for forming the cross-linked gel 10 can betailored to avoid causing detrimental effects to the beneficialproperties of the omega-3 fatty acids, or at least effects toodetrimental to have any lasting effect. As described herein, certainproperties of the fatty acids may lose their effectiveness, howeverother desired properties are maintained. If there is no concern formaintaining the beneficial effects, the curing and other steps leadingto the formation of the cross-linked gel 10 can include steps that mayreduce some of the beneficial properties of the omega-3 fatty acids, asunderstood by one of ordinary skill in the art. Example embodimentsillustrating the formation and different configurations of thecross-linked gel 10 are provided herein.

The cross-linked gel 10 of the present invention serves as anon-polymeric biological oil based cross-linked gel and can also serveas a physical cross-linked gel if sufficiently cured. In accordance withthe example embodiments described herein, the cross-linked gel is formedof a non-polymeric cross-linked gel derived from fatty acid compounds.The fatty acid compounds include omega-3 fatty acids when the oilutilized to form the cross-linked gel is fish oil or an analog orderivative thereof. As liquid fish oil is heated, autoxidation occurswith the absorption of oxygen into the fish oil to create hydroperoxidesin an amount dependent upon the amount of unsaturated (C═C) sites in thefish oil. However, the (C═C) bonds are not consumed in the initialreaction. Concurrent with the formation of hydroperoxides is theisomerization of (C═C) double bonds from cis to trans in addition todouble bond conjugation. It has been demonstrated that hydroperoxideformation increases with temperature. Heating of the fish oil allows forcross-linking between the fish oil unsaturated chains using acombination of peroxide (C—O—O—C), ether (C—O—C), and hydrocarbon (C—C)bridges. The formation of the cross-links results in gelation of thecross-linked gel after the (C═C) bonds have substantially isomerizedinto the trans configuration. The (C═C) bonds can also form C—Ccross-linking bridges in the glyceride hydrocarbon chains using aDiels-Alder Reaction. In addition to solidifying the cross-linked gelthrough cross-linking, both the hydroperoxide and (C═C) bonds canundergo secondary reactions converting them into lower molecular weightsecondary oxidation byproducts including aldehydes, ketones, alcohols,fatty acids, esters, lactones, ethers, and hydrocarbons.

The non-polymeric cross-linked gel derived from fatty acid compounds,such as those of fish oil, includes a cross-linked structure oftriglyceride and fatty acid molecules in addition to free and boundglycerol, monoglyceride, diglyceride, and triglyceride, fatty acid,anhydride, lactone, aliphatic peroxide, aldehyde, and ketone molecules.There are a substantial amount of ester bonds remaining after curing inaddition to peroxide linkages forming the majority of the cross-links inthe gel. The cross-linked gel degrades into fatty acid, short and longchain alcohol, and glyceride molecules, which are all non-inflammatoryand likewise consumable by cells in the soft tissue to which thecross-linked gel is applied. Thus, the cross-linked gel isbio-absorbable.

UV initiated curing (photo-oxygenation) in accordance with the presentinvention involves the interaction between a double bond and singletoxygen produced from ordinary triplet oxygen by light and typically inthe presence of a sensitizer such as chlorophyll or methylene blue andresults in the formation of hydroperoxides. The chemical reaction isdescribed in the following graphic.

Since the above described reaction is not a radical chain process, itpossess no induction period and is typically unaffected by antioxidantscommonly used to inhibit autoxidation. However, this reaction can beinhibited by single oxygen quenchers such as carotene. This reaction islimited to C═C carbon atoms and results in a conversion from cis totrans C═C isomers during curing (as occurs with heat initiated curing).However, photo-oxygenation using UV is a relatively quicker reactionthan autoxidation from heat curing, in the realm of about 1000-1500times faster. The quicker reaction especially holds true for methyleneinterrupted polyunsaturated fatty acids, such as EPA and DHA, which arefound in the fish oil based embodiments of the present invention.

An important aspect of UV curing when compared to heat curing is thatalthough the byproducts obtained by both curing methods are similar,they are not necessarily identical in amount or chemical structure. Onereason for this is due to the ability of photo-oxygenation to createhydroperoxides at more possible C═C sites as shown for linolenate in thebelow graphic.

Photo-oxygenation, such as that which results from UV curing, due to itsenhanced ability to create inner hydroperoxides, also results in theability to form relatively greater amounts of cyclic byproducts, whichalso relates to peroxide cross-linking between fish oil hydrocarbonchains. For example, photo-oxygenation of linolenate results in 6different types of hydroperoxides to be formed where autoxidationresults in only 4. The greater amount of hydroperoxides created usingphoto-oxygenation results in a similar, but slightly different,structure and amount of secondary byproducts to be formed relative toautoxidation from heat curing. Specifically, these byproducts arealdehydes, ketones, alcohols, fatty acids, esters, lactones, ethers, andhydrocarbons.

FIGS. 2A, 2B, and 2C illustrate side views of multiple differentembodiments of the cross-linked gel 10 when cured. In FIG. 2A, across-linked gel 10A is shown having two tiers, a first tier 20 and asecond tier 22. The first tier 20 and the second tier 22 as shown areformed of different materials. The different materials can be differentforms of fish oil, different naturally occurring oils other than fishoil, or therapeutic components as will be discussed later herein. Thedifferent materials bind together to form the cross-linked gel 10A.

FIG. 2B shows a cross-linked gel 10B having a first tier 24, a secondtier 26, and a third tier 28. In the embodiment shown, each of the tiers24, 26, and 28 is formed of the same material. The plurality of tiersindicates the ability to create a thicker cross-linked gel 10 ifdesired. The greater the number of tiers, the thicker the resulting gel.The thickness of the cross-linked gel 10 can have an effect on theoverall strength and durability of the cross-linked gel 10. A thickergel is generally stronger and more durable. In addition, the thicknessof the cross-linked gel 10 can also affect the duration of time that thecross-linked gel 10 lasts after implantation. A thicker cross-linked gel10 provides more material to be absorbed by the body, and thus will lastlonger than a thinner cross-linked gel 10. One of ordinary skill in theart will appreciate that the thickness of the cross-linked gel 10 canvary both by varying the thickness of each tier 24, 26, and 28, and byvarying the number of tiers 24, 26, and 28. Accordingly, the presentinvention is not limited to the particular layer combinationsillustrated.

FIG. 2C shows another cross-linked gel 10C, having four tiers, a firsttier 30, a second tier 32, a third tier 34, and a fourth tier 36. Inthis example embodiment, the first tier 30 and the third tier 34 areformed of the same material, while the second tier 32 and the fourthtier 36 are formed of a material different from each other and differentform that of the first tier 30 and the third tier 34. Accordingly, thisembodiment illustrates the ability to change the number of tiers, aswell as the material used to form each of the tiers 30, 32, 34, and 36.Again, the different materials can be derived from different forms offish oil, different naturally occurring oils other than fish oil, ortherapeutic components as will be discussed later herein.

FIGS. 3A through 3F show additional embodiments or configurations of thecross-linked gel 10. The embodiments include cross-linked gel 10D in acircular configuration, cross-linked gel 10E in an oval configuration,cross-linked gel 10F in a U-bend configuration, cross-linked gel 10G ina square configuration having a circular aperture, cross-linked gel 10Hin a wave configuration, and cross-linked gel 10I in an irregular shapeconfiguration. Each of the configurations of the cross-linked gel 10Dthrough 10I represent different types of configurations. Theconfigurations illustrated are by no means the only possibleconfigurations for the cross-linked gel 10. One of ordinary skill in theart will appreciate that the specific shape or configuration of thecross-linked gel 10 can vary as desired. A more prevalent configurationis the rectangular or oblong configuration of FIG. 1. However, FIGS. 3Athrough 3F illustrate a number of different alternative embodiments, andindicate some of the many possible configurations.

FIG. 4 is a flowchart illustrating one example method for the formationof the cross-linked gel 10. A surface is provided having a release agent(step 100). The surface can be prepared by the application of therelease agent, or the release agent can be pre-existing. The releaseagent can be a number of different solutions, including for example,polyvinyl alcohol (PVA). The release agent can be applied in a number ofdifferent ways as well, including but not limited to spraying, dipping,coating, painting, and the like. It should be noted that the releaseagent can be applied to the surface immediately prior to the remainingsteps or well in advance of the remaining steps, so long as when theremaining steps are executed there is a release agent on the surface.

An oil component is applied to the surface on top of the release agent(step 102). As noted previously, the oil component can be a naturallyoccurring oil, such as fish oil, cod liver oil, cranberry oil, or otheroils having desired characteristics. In addition, the oil component canbe an oil composition, meaning a composition containing oil in additionto other substances. For example, the oil composition can be formed ofthe oil component in addition to a solvent and/or a preservative.Solvents can include a number of different alternatives, includingethanol or N-Methyl-2-Pyrrolidone (NMP). The preservative can alsoinclude a number of different alternatives, including vitamin Ecompounds. One of ordinary skill in the art will appreciate that thereare a number of different solvents and preservatives available for usewith the oil component to form the oil composition, and as such thepresent invention is not limited to only those listed in the examplesherein. The solvent can be useful to alter the physical properties ofthe oil, as well as prepare the oil for combination with a therapeuticagent as described below. The preservative can also be useful inaltering the physical properties of the oil component, as well asprotecting some of the beneficial properties of the oil component duringcertain curing processes. Such beneficial properties include the healingand anti-inflammatory characteristics previously mentioned.

The oil component can be combined with one or more therapeutic agents toform an oil composition. Thus, if the added therapeutic benefit of aparticular therapeutic agent or agents is desired, the therapeuticagent(s) can be added to the oil component prior to application to thesurface, along with the oil component during application to the surface(including mixing with the oil component prior to application), or afterthe oil component has been applied (step 104). The differentalternatives for adding the therapeutic agent(s) are determined in partbased on the desired effect and in part on the particular therapeuticagent(s) being added. Some therapeutic agents may have reduced effect ifpresent during a subsequent curing step. Some therapeutic agents may bemore useful intermixed with the oil component to extend the releaseperiod, or applied to the surface of the oil component, resulting in afaster release because of increased exposure. One of ordinary skill inthe art will appreciate that a number of different factors, such asthose listed above in addition to others, can influence when in theprocess the therapeutic agent is added to the oil component, or thecross-linked gel 10. Accordingly, the present invention is not limitedto the specific combinations described, but is intended to anticipateall such possible variations for adding the therapeutic agent(s).

For example, if 80% of a therapeutic agent is rendered ineffectiveduring curing, the remaining 20% of therapeutic agent, combined with anddelivered by the barrier can be efficacious in treating a medicaldisorder, and in some cases have a relatively greater therapeutic effectthan the same quantity of agent delivered with a polymeric or other typeof coating or barrier. This result can be modified with the variance ofalpha-tocopherol to protect the therapeutic agent during the curingprocess, and then slow and extend the delivery of the therapeutic agentduring absorption of the barrier layer into the tissue.

The oil component (or composition if mixed with other substances) isthen hardened into the cross-linked gel 10 (step 106). The step ofhardening can include hardening, or curing, such as by introduction ofUV light, heat, oxygen or other reactive gases, chemical curing, orother curing or hardening method. The purpose of the hardening or curingis to transform the more liquid consistency of the oil component or oilcomposition into a more solid film or gel, while still maintainingsufficient flexibility to allow bending and wrapping of the film or gelas desired. However, the hardening process as described herein does notrefer to or include the process of hydrogenation.

After the cross-linked gel 10 has formed, another determination is madeas to whether therapeutic agents should be applied to the gel. Ifdesired, the therapeutic agent(s) is added to the cross-linked gel 10(step 108). Subsequently, the cross-linked gel 10 is removed from thesurface (step 110). Once again, there is opportunity to apply atherapeutic agent(s) to the cross-linked gel 10 on one or both sides ofthe cross-linked gel 10. If such therapeutic agent(s) is desired, thetherapeutic agent(s) is applied (step 112). The additional therapeuticagent can also be applied in the form of a non-cured or minimally curedoil, such as fish oil. The oil can likewise include other therapeuticagents mixed therewith. The resulting structure of such an applicationforms the underlying cross-linked gel 10 that is cured to form the gel,with a top coating of oil and potentially additional therapeutic agentlayered on top. This structure enables the provision of a short termrelease of therapeutic from the oil top layer combined with a longerterm release from the cured gel, which takes more time to degrade.

After application of the therapeutic agent(s), or after the cross-linkedgel 10 is removed from the surface, the cross-linked gel 10 issterilized. The sterilization process can be implemented in a number ofdifferent ways. For example, sterilization can be implemented utilizingethylene oxide, gamma radiation, E beam, gas plasma, or vaporizedhydrogen peroxide (VHP). One of ordinary skill in the art willappreciate that other sterilization processes can also be applied, andthat those listed herein are merely examples of sterilization processesthat result in a sterilization of the cross-linked gel 10, preferablywithout having a detrimental effect on the cross-linked gel.

It should be noted that the oil component or oil composition can beadded multiple times to create multiple tiers in forming thecross-linked gel 10. For example, if a thicker cross-linked gel 10 isdesired, additional tiers of the oil component or oil composition can beadded after steps 100, 104, 106, 108, 110, or 112. Different variationsrelating to when the oil is hardened and when other substances are addedto the oil are possible in a number of different process configurations.Accordingly, the present invention is not limited to the specificsequence illustrated. Rather, different combinations of the basic stepsillustrated are anticipated by the present invention.

FIGS. 5A and 5B illustrate the cross-linked gel 10 and a medical devicein the form of a mesh 40. In FIG. 5A, the cross-linked gel 10 and mesh40 are shown in exploded view, while FIG. 5B shows the cross-linked gel10 coupled with the mesh 40. The mesh 40 is merely one example medicaldevice that can be coupled with the cross-linked gel 10. In the instanceof the mesh 40, it can be useful to have one side of the mesh support arougher surface to encourage tissue in-growth, and the other side of themesh with an anti-adhesion, non-inflammatory, and/or anti-inflammatorysurface to prevent the mesh from injuring surrounding tissue or causinginflammation. The coupling of the cross-linked gel 10 with the mesh 40achieves such a device.

As understood by one of ordinary skill in the art, the properties of themesh 40 and the cross-linked gel 10 can vary. There may be a requirementfor the mesh 40 to have one side, or a portion of a side, that hasanti-adhesion properties for a period of several days. Alternatively,multiple sides of the mesh 40 may be required to have anti-adhesionproperties. As such, the cross-linked gel 10 can be applied to allsides, or portions of sides, or portions of one side of the mesh 40.

In addition, the requirement may be for the anti-adhesion properties tolast several weeks, or even longer. Accordingly, the rate of degradationcan also be varied by changing such properties as amount ofcross-linking, thickness, and existence of additives, such as vitamin Ecompounds to achieve longer or shorter term anti-adhesion properties. Inaddition, there may be a desire to include a therapeutic agent to reduceinflammation, provide antibiotic therapy, or other therapeutic measures,in combination with the use of the mesh 40. Accordingly, the therapeuticagent(s) can be added to the cross-linked gel 10 to achieve the desiredcontrolled release of the therapeutic agent after implantation. Aspreviously described, combinations of cured oils top coated with lessercured or non-cured oils and therapeutic agents can form the cross-linkedgel 10.

The particular properties or characteristics of the mesh 40 aredetermined based on the desired use of the mesh 40. A commonimplementation is for the mesh 40 to be formed of a bio-compatiblematerial, such as polypropylene, however other bio-compatible materialscan be utilized, such as a mesh formed of the same or similar substanceas the cross-linked gel 10 (i.e., oil based).

FIG. 6 is a flowchart illustrating one example method for forming themesh 40 and cross-linked gel 10 combination. The medical device isprovided (step 150). The medical device can be, for example, the mesh40, or a graft 50, a catheter balloon 52, a stent 54, as shown in FIGS.8A through 8C, or another form of medical device as would be understoodby one of ordinary skill in the art.

A determination is made as to whether a release agent should be added tothe medical device to aid in removing the device from its location(e.g., on a surface) after combination with the cross-linked gel 10. Ifa release agent is required, the release agent is applied to the medicaldevice (step 152). An example release agent for such an application ispolyvinyl alcohol.

The medical device is then combined with the cross-linked gel 10 (step154). Depending on the particular medical device, the combination withthe cross-linked gel 10 can be implemented more efficiently by eitherapplying the cross-linked gel 10 to the medical device, or placing themedical device on the cross-linked gel 10. For example, in the case ofthe mesh 40, the mesh 40 can be placed on top of the cross-linked gel10, or the cross-linked gel 10 can be placed on top of the mesh 40.

The medical device and the cross-linked gel are then cured to create abond (step 156). The curing process can be one of several knownprocesses, including but not limited to applying heat, or UV light, orchemical curing, to cure the cross-linked gel. After curing, if there isany release agent present, the release agent is washed away using water,or some other washing agent (step 158).

FIG. 7 is a flowchart illustrating another example method of forming amedical device with a cross-linked gel. A surface is prepared with arelease agent, such as PVA (step 170). The medical device is placed onthe surface (step 172). The oil component or oil composition is appliedto the medical device (step 174). The oil component or oil compositioncan be, for example, poured or sprayed onto the medical device. Thecombined oil component/composition and medical device are then cured(step 176) using methods such as application of heat, UV light, oxygen,chemical cross-linker, or hardening processes, to form the cross-linkedgel in combination with the medical device. The combined cross-linkedgel and mesh are then removed from the surface (step 178) and therelease agent is washed away (step 180).

As with the method of FIG. 6, if desired, a therapeutic agent can beadded to the oil component or oil composition at any point along theprocess forming the combined cross-linked gel 10 and medical device,including being a component of the oil composition. As discussedpreviously, consideration must be given as to whether the therapeuticagent may be affected by the curing process, or other aspects of theprocess.

Furthermore, the formation of the oil composition can be done inaccordance with different alternatives to the methods described. Forexample, prior to forming the cross-linked gel 10, a preservative, suchas Vitamin E compounds can be mixed with the naturally occurring oilcomponent to form the oil composition. A solvent can be mixed with atherapeutic agent, and then added to the naturally occurring oil to formthe oil composition. The solvent can be chosen from a number ofdifferent alternatives, including ethanol or N-Methyl-2-Pyrrolidone(NMP). The solvent can later be removed with vacuum or heat. Othersolvent alternatives can include, but are not limited to, a solvent ormixture of solvents including solvents that are generally acceptable forpharmaceutical use. Suitable solvents include, for example: alcohols andpolyols, such as C₂-C₆ alkanols, 2-ethoxyethanol, ethanol, isopropanol,butanol, benzyl alcohol, ethylene glycol, propylene glycol, butanediolsand isomers thereof, glycerol, pentaerythritol, sorbitol, mannitol,transcutol, dimethyl isosorbide, polyethylene glycol, and polypropyleneglycol; amides, such as 2-pyrrolidone, 2-piperidone, 2-caprolactam,N-alkylpyrrolidone, N-methyl-2-pyrrolidone, N-hydroxyalkylpyrrolidone,N-alkylpiperidone, N-alkylcaprolactam, dimethylacetamide; esters, suchas ethyl acetate, methyl acetate, butyl acetate, ethylene glycol diethylether, ethylene glycol dimethyl ether, propylene glycol dimethyl ether,ethyl proprionate, tributylcitrate, acetyl triethylcitrate, acetyltributyl citrate, triethylcitrate, ethyl oleate, ethyl caprylate, ethylcutyrate, tracetin, ε-caprolactone and isomers thereof, δ-valerolactorneand isomers thereof, β-butyrolactone and isomers thereof; and othersolvents, such as water, dimethylsulfoxide, benzyl benzoate, ethyllactate, acetone, methylethyl ketone, dimethylsolfone, tetrahydrofuran,decylmethylsufoxide, N,N-diethyl-m-toulamide or1-dodecylazacycloheptan-2-one, hexane, chloroform, dichloromethane.

In addition, it should again be noted that the oil component or oilcomposition can be added multiple times to create multiple tiers informing the cross-linked gel 10. If a thicker cross-linked gel 10 isdesired, additional tiers of the oil component or oil composition can beadded after steps 174 and 176. Different variations relating to when theoil is hardened and when other substances are added to the oil arepossible in a number of different process configurations. Accordingly,the present invention is not limited to the specific sequenceillustrated. Rather, different combinations of the basic stepsillustrated are anticipated by the present invention.

Depending on the type of therapeutic agent component, the resultingcross-linked gel 10 can maintain its bio-absorbable characteristics ifthe therapeutic agent component is also bio-absorbable.

The therapeutic agent component, as described herein, has some form oftherapeutic or biological effect. The oil component or oil compositioncomponent can also have a therapeutic or biological effect.Specifically, the cross-linked gel 10 (and its oil constituents) enablethe cells of body tissue of a patient to absorb the cross-linked gel 10itself, rather than breaking down the gel and disbursing by-products ofthe gel for ultimate elimination by the patient's body.

As previously stated, and in accordance with embodiments of the presentinvention, the cross-linked gel 10 is formed of a naturally occurringoil, or composition including a naturally occurring oil, such as fishoil, cod liver oil, cranberry oil, and the like. A characteristic of thenaturally occurring oil is that the oil includes lipids, whichcontributes to the lipophilic action described later herein, that ishelpful in the delivery of therapeutic agents to the cells of the bodytissue. In addition, the naturally occurring oil can include theessential omega-3 fatty acids in accordance with several embodiments ofthe present invention.

It should also be noted that the present description makes use of themesh 40 as an example of a medical device that can be combined with thecross-linked gel 10 of the present invention. However, the presentinvention is not limited to use with the mesh 40. Instead, any number ofother implantable medical devices can be combined with the cross-linkedgel 10 in accordance with the teachings of the present invention. Suchmedical devices include catheters, grafts, balloons, prostheses, stents,other medical device implants, and the like. Furthermore, implantationrefers to both temporarily implantable medical devices, as well aspermanently implantable medical devices.

FIGS. 8A, 8B, and 8C illustrate some of the other forms of medicaldevices mentioned above in combination with the cross-linked gel 10 ofthe present invention. FIG. 8A shows a graft 50 with the cross-linkedgel 10 coupled or adhered thereto. FIG. 8B shows a catheter balloon 52with the cross-linked gel 10 coupled or adhered thereto. FIG. 8C shows astent 54 with the cross-linked gel 10 coupled or adhered thereto. Eachof the medical devices illustrated, in addition to others notspecifically illustrated or discussed, can be combined with thecross-linked gel 10 using the methods described herein, or variationsthereof. Accordingly, the present invention is not limited to theexample embodiments illustrated. Rather the embodiments illustrated aremerely example implementations of the present invention.

Returning to the step of curing as described herein, the step can have anumber of different variations and permutations that ultimatelyinfluence the properties of the resulting cured cross-linked gel, andany therapeutic agents if include therein. In this instance making useof a naturally occurring oil, such as fish oil, such oils or oilcompositions as described herein can be heated to increase viscosity.The level of UV light and the time duration of exposure of the oil oroil composition will affect how viscous the oil or oil compositionbecomes.

In addition, combining pre-cured, highly viscous oil with untreated oilresults in a faster cure time of the resulting combination when formingthe cross-linked gel. Also, taking a pre-cured oil and decreasing itsviscosity slightly with solvent will result in a faster cure time aswell. To demonstrate the effectiveness of a combination of UV and heatfrom UV curing relative to exclusive heat curing, the following exampleis provided.

EXAMPLE #1

UV light was utilized to initiate curing in fish oil. No sensitizer wasadded to the fish oil during UV curing. In addition, the UV lamps usedwere of relatively low power (15W at 252 nm) and reached a temperatureof 88-90° F. during curing. Thus, the films cured using the UV processdescribed here were cured using a combination of photo-oxygenation andautoxidation initiation pathways. Also, since no sensitizer was addeddirectly to the fish oil to create the singlet oxygen needed to cure thefish oil, the kinetics of the process are similar, but at a lowerefficiency.

An FTIR spectrum analysis for heat and UV-heat cured fish oil coatingsencapsulating polypropylene mesh was performed. The heat cured meshcoating was created by heating the coating at 200° F. for 48 hours in ahigh airflow oven. The UV-heat cured mesh coating was created by curingfor 29 hours with the “rough side” of the mesh facing up toward the UVlamp (15 W at 252 nm, temperature of chamber 88-90° F.), followed byflipping the mesh over for an additional 19 hours, with a total curingtime of 48 hours. There was no high airflow used in the UV-air curingexperiment.

The resulting cured coatings had several differences. The trans C═Cbonds were almost completely consumed using the UV-heat curing method;whereas they were still present using heat curing alone. In addition,the UV-heat curing spectrum possess more OH bands (indicative of alcoholand fatty acid byproduct formation), less CH2 band intensity, greateranhydride/aliphatic peroxide/lactone cross-linking, and more fattyacid/ketone C═O absorption, relative to the purely heat cured coating.Also, similar to the heat cured fish oil coating, a majority of theester bonds of the fish oil triglyceride headgroup are retained usingthe UV-heat curing method.

The coating of the UV-heat curing method contains a greater amount ofoxidized byproducts than the coating of the heat cured method, asevidenced by greater OH (alcohol and fatty acid) and fatty acid/ketoneC═O bands. In addition, due to the increase in hydroperoxide formationdue to photo-oxygenation chemistry, there is a greater amount ofanhydride/aliphatic peroxide/lactone cross-linking absorption.Furthermore, there are a greater amount of carbon-carbon cross-linking,and the UV-heat cured mesh coating contains shorter hydrocarbon chainlengths than the heat cured method.

As evidenced by the examples herein, by using UV light in addition toheat, the fish oil curing chemistry can differ in the resulting coatingsprepared over a similar time frame. Specifically, the UV-heat curedcoating possesses greater amounts of oxidized byproducts, greateramounts of cross-linking, and shorter hydrocarbon chain segments.Ultimately, the resulting coating having been cured by UV-heat degradesin a manner that releases drugs contained therein in a similar butdifferent manner to the heat cured coatings. The below examplesillustrate this relationship.

EXAMPLE #2 UV-Cured: Cyclosporine a Drug Delivery on Encapsulated Mesh

A fish oil and CSA encapsulated mesh was manufactured using UV lamps (15watts, at 88-90° F.) for 48 hours, using 125 ul of formulation per 1×1″sample. Some “pin holes” were observed in the coating. The formulationwas 2.85% CSA in Fish Oil with no solvent, but with heating at 37° C.for 1 hour with vortexing. An average amount extracted after curing (asmeasured by HPLC) was 265 micrograms. Based on coating weight, thisrepresents an 8% CSA survival rate. The graph of FIG. 10 shows thedissolution rate of the cured coating.

EXAMPLE #3 Heat-Cured: Comparison of Cyclosporine A—Pure Fish OilEncapsulated Mesh Coatings Using 200° F. and 150° F. Curing

A coated mesh was manufactured with a formulation of 2.84% Cyclosporinein Fish Oil. No solvent was used, and Cyclosporine was soluble in thefish oil with slight heating at 37° C. One coating was heated for 3 daysat 150° F. and a second coating was heated for 24 hours at 200° F. Aftercuring, drug loading was about 478 ug (14.22% recovery) for the 200° F.cured mesh and about 1158 ug (26.00% recovery) for the 150° F. curedmesh. The coatings were then degraded and the drug release measured asillustrated in the graph of FIG. 11. It is noted that the amountrecovered is dependent on the coating weight and amount of drug detectedusing HPLC methods after drug extraction from the cured fish oilcoating.

Based on the measured results of the above two examples of curing, thefirst being two variations of heat curing and the second being avariation of UV curing, the graph of FIG. 12 compares the degradation ofthe coatings.

The graph of FIG. 12 illustrates that the 150° F. cured coating, whichhas less cross-linking, results in a faster drug release than the 200°F. cured coating, which possess more cross-linking. This exampledemonstrates the ability to load an anti-proliferative, Cyclosporine A,into cured fish oil encapsulated mesh coatings and by using temperatureto control the cross-linking properties of that coating, the drugdissolution release profile is significantly altered. The UV-curedcoating shows a dissolution profile that is more rapid that the 200° F.cured mesh, but slower than the 150° F. cured mesh.

EXAMPLE #4 UV-Cured Rapamycin Drug Delivery on Encapsulated Mesh

A coated mesh (mesh structure encapsulated in the coating) wasmanufactured and cured using UV lamps (15 watts, at 88-90° F.) for 48hours. An amount of 125 ul of formulation was used per 1×1″ sample. Some“pin holes” were observed in the coating. The formulation was about4.58% Rapamycin in Fish Oil (where the percentage was based on noremaining nMP in formulation, where any trace amounts should be removedafter curing). An average amount of drug was extracted based on HPLCanalysis in the amount of about 611 micrograms. Based on coating weight,this represents an 18% Rapamycin survival rate. The degradation and drugrelease is depicted in the graph of FIG. 13.

EXAMPLE #5 Heat Cured Rapamycin Drug Delivery in Encapsulated Fish OilMesh Using 150° F. Curing Conditions

A formulation of about 4.88% Rapamycin (after solvent removal) in fishoil was provided in the coating. The coating was cured by heating for 3days at 150° F. Initial drug loading measured after curing using HPLCwas about 378 ug. The coating was degraded and drug release measured asdepicted in the graph of FIG. 14. It is noted that the amount recoveredis dependent on the coating weight and amount of drug detected usingHPLC methods after drug extraction from the cured fish oil coating.

Based on the measured results of the above two examples of curing, thefirst being two UV-heat curing and the second being a variation of heatcuring, the graph of FIG. 15 compares the degradation of the coatings.

These results demonstrate that UV-cured fish oil coatings may result ina faster dissolution than 150° F. heat-cured coatings when loadingRapamycin in the coating.

In view of the above examples, the previously described methods ofmanufacture that include a curing step can be implemented using aUV-heat curing approach. In accordance with the method of the presentinvention, the curing process (such as referred to in step 156 in FIG. 6and step 176 in FIG. 7 of the present description) can be modified toresult in different cross-linked gels. The process can be implementedusing heat, as previously described, or can be implemented usingUV-heat. Given the rate of degradation of the UV-heat cured coating, ifa desired rate of coating degradation approximates the rates achievableby UV-heat curing, then UV-heat curing can be utilized. In addition, ifa greater amount of oxidized byproducts, greater amounts ofcross-linking, and shorter hydrocarbon chain segments, then UV-heatcuring can be selected over heat curing. It should be appreciated thatthe intensity and duration of the UV light can be varied to alter thecuring process, as desired. Generally speaking, a greater intensity fora greater duration will result in more cross-linking and more completecuring of the oil or substance being cured versus a lesser intensity anda lesser duration, which will result in fewer total cross-linking.

FIG. 9 shows a flowchart in which considerations are made during thecuring process to result in a cured or partially cured cross-linked gelthat has specific desired characteristics. In accordance with the methodof the present invention, the curing process (such as referred to instep 156 in FIG. 6 and step 176 in FIG. 7 of the present description)can be modified to result in different cross-linked gels. At some pointin time prior to beginning the curing portion of the process, adetermination is made as to whether a relatively fast but shorter termdegradation (corresponding to a faster drug release rate when a drug isincluded) is desired, or a relatively slower but longer term degradation(corresponding to a slower drug release rate when a drug is included) isdesired (step 190). If a relatively faster but shorter term drug releaserate is desired, a determination is made to cure in a manner that willresult in an amount of cross-links relatively lesser than otherwisepossible (step 192). If a relatively slower but longer term drug releaserate is desired, a determination is made to cure in a manner that willresult in an amount of cross-links relatively greater than the shorterterm drug release rate amount, and relatively closer to a maximumpossible amount of cross-links to form the gel (step 194).

In general, a higher UV light intensity will result in a greater numberof cross-links than a lower UV light intensity. Furthermore, in general,a relatively longer duration of cure time will result in a greaternumber of cross-links than a relatively shorter duration of cure time.

Modifying the starting pre-cured viscosity or pre-cured oilconcentration in the mixture will enhance the curing speed. One ofordinary skill in the art will appreciate that the scope of the presentinvention is not limited to only coating on the mesh, but rather hasapplication to other medical devices, or as a stand-alone film.

The curing conditions utilized, such as the duration of time and theintensity of UV light can influence the amount of cross-linking thatoccurs in the cross-linked gel (i.e., the cross-link density). Curedfish oil coatings enable regulation of the release profile ofdrug-loaded oil-based coatings from implantable devices. The releaseprofile can be controlled through changes in oil coating chemistry byvarying coating composition, UV light intensity, and cure times. Theposition of the drug-containing layer on the coated device provides anadditional mechanism to alter the release profile of the drug-loadedfish oil coating. This can be achieved by either loading the drug intothe encapsulating base layer of the device, or by coating a topcoatoverlayer coating onto the previously cured encapsulating base layer.

More specifically, curing conditions utilized to form the cross-links,such as time and intensity can influence the amount of coatingcross-linking density and byproduct formation, which in turn effects thecoating degradation. Thus, by altering the curing conditions employed,the dissolution rate of the therapeutic compound of interest is alsoaltered.

Furthermore, the oil component itself, in the form of fish oil forexample, can provide therapeutic benefits in the form of reducedinflammation, and improved healing, if the fish oil composition is notsubstantially modified during the process that takes the naturallyoccurring fish oil and forms it into the cross-linked gel 10. Some priorattempts to use natural oils as coatings have involved mixing the oilwith a solvent, or curing the oil in a manner that destroys thebeneficial aspects of the oil. The solvent utilized in the examplecross-linked gel 10 embodiment of the present invention (NMP) does nothave such detrimental effects on the therapeutic properties of the fishoil. Thus the benefits of the omega-3 fatty acids, and the EPA and DHAsubstances are substantially preserved in the cross-linked gel of thepresent invention.

Therefore, the cross-linked gel 10 of the present invention includes thebio-absorbable naturally occurring oil (i.e., fish oil). Thecross-linked gel 10 is thus able to be absorbed by the cells of the bodytissue. With the present invention, because of the lipophilic actionenabled by the bio-absorbable lipid based cross-linked gel 10 of thepresent invention, the intake by the tissue cells of the cross-linkedgel 10, and any therapeutic agent component, is substantially controlledby the cells themselves. In configurations using polymer basedmaterials, the drugs were released at a rate regardless of the reactionor need for the drug on the part of the cells receiving the drug. Withthe cross-linked gel 10 of the present invention, the cells can intakeas much of the cross-linked gel 10, and correspondingly the therapeuticagent, as is needed by the damaged cell requiring treatment.

In addition, the bio-absorbable nature of the cross-linked gel 10results in the cross-linked gel 10 being completely absorbed over timeby the cells of the body tissue. There is no break down of thecross-linked gel 10 into sub parts and substances that are inflammatoryand are eventually distributed throughout the body and in some instancesdisposed of by the body, as is the case with biodegradable syntheticpolymer coatings. The bio-absorbable nature of the cross-linked gel 10of the present invention results in the cross-linked gel 10 beingabsorbed, leaving only the medical device structure, if the cross-linkedgel 10 is not implanted alone. There is no foreign body inflammatoryresponse to the cross-linked gel 10.

In addition, the cross-linked gel 10 provides a lubricious oranti-adhesive surface against tissue. The cross-linked gel 10 itself canprovide an anti-adhesion barrier between two sections of tissue, or thecross-linked gel 10 can form an anti-adhesion surface on a medicaldevice, such as the mesh 40. The use of the naturally occurring oil,such as fish oil, provides extra lubrication to the surface of themedical device, which helps to reduces injury. With less injury, thereis less of an inflammatory response, and less healing required. Likewisethe fatty acid derived cross-linked gel that makes up the cross-linkedgel maintains anti-inflammatory properties and non-inflammatoryproperties, which also substantially lowers the inflammatory response ofthe tissue. The reduced inflammation also reduces adhesions.

Numerous modifications and alternative embodiments of the presentinvention will be apparent to those skilled in the art in view of theforegoing description. Accordingly, this description is to be construedas illustrative only and is for the purpose of teaching those skilled inthe art the best mode for carrying out the present invention. Details ofthe structure may vary substantially without departing from the spiritof the invention, and exclusive use of all modifications that comewithin the scope of the appended claims is reserved. It is intended thatthe present invention be limited only to the extent required by theappended claims and the applicable rules of law.

What is claimed is:
 1. An ultraviolet (UV) light cured gel, the gelcomprising: fish oil, wherein the fish oil comprises unsaturated fattyacids; wherein the fish oil is in a state of having been cured byapplication of UV light to cross link the unsaturated fatty acids byester bonds in a substantially random configuration to form the gel;wherein the gel is bioabsorbable; wherein the gel further comprises atherapeutic agent; and wherein the amount of curing is controlled by theapplication of the UV light in such a way that the gel is configured toprovide controlled release of the therapeutic agent.
 2. An ultraviolet(UV) light cured gel, the gel comprising: fish oil, wherein the fish oilcomprises unsaturated fatty acids; wherein the fish oil is in a state ofhaving been cured by application of UV light to cross link theunsaturated fatty acids by ester bonds in a substantially randomconfiguration to form the gel; wherein the gel is bioabsorbable; whereinthe gel further comprises a therapeutic agent; and wherein followingimplantation of the gel in a patient, the gel degrades and therebyreleases the therapeutic agent.
 3. The gel of claim 2, wherein the fishoil comprises at least a partially cured oil or oil composition.
 4. Thegel of claim 2, wherein the gel is configured to release the therapeuticagent over at least about seven days following implantation.
 5. The gelof claim 4, wherein the gel is formed with application of UV light at252 nm.
 6. The gel of claim 4, wherein the gel is formed withapplication of UV light for 48 hours.
 7. The gel of claim 4, wherein thegel is formed with application of UV light at 252 nm for 48 hours. 8.The gel of claim 2, wherein the gel is configured to provide controlledrelease of the therapeutic agent.
 9. The gel of claim 2, wherein the gelexhibits at least one property selected from the group consisting ofanti-inflammatory properties, non-inflammatory properties, and woundhealing properties.
 10. The gel of claim 2, wherein the gel has beensterilized with a method of sterilization selected from the group ofmethods of sterilization consisting of ethylene oxide, gamma radiation,e-beam, steam, gas plasma, and vaporized hydrogen peroxide (VHP). 11.The gel of claim 2, wherein the gel is configured as a coating on amedical device or as a stand-alone film.
 12. The gel of claim 2, whereinthe fish oil is pre-treated to increase viscosity prior to curing. 13.The gel of claim 2, further comprising vitamin E.
 14. An ultraviolet(UV) light cured gel, the gel comprising: fish oil, wherein the fish oilcomprises unsaturated fatty acids; wherein the fish oil is in a state ofhaving been cured by application of UV light to cross link theunsaturated fatty acids by ester bonds in a substantially randomconfiguration to form the gel; wherein the gel is bioabsorbable; whereinthe gel further comprises an anti-proliferative agent; and whereinfollowing placement of the gel in a 0.01M PBS solution, the gel degradesand thereby releases the anti-proliferative agent.
 15. The gel of claim2, wherein the therapeutic agent is selected from the group consistingof antioxidants, anti-inflammatory agents, anti-coagulant agents, drugsto alter lipid metabolism, anti-proliferatives, anti-neoplastics, tissuegrowth stimulants, functional proteins, anti-infective agents, imagingagents, anesthetic agents, chemotherapeutic agents, tissue absorptionenhancers, anti-adhesion agents, germicides, analgesics, andantiseptics.